IR Polished KRS5 Thallium Bromide Iodide Window 50mm Ø x 4mm

KRS5, a deep infrared material with a high refractive index, is widely used in ATR prisms, windows, and lens spectroscopy. When combined with germanium, KRS5 can also be utilized in athermalized IR imaging systems. KRS-5 is produced using the sealed Stockbarger crystal growth technique. The highest purity starting materials are selected to ensure no anionic absorption bands between 2 μm and 16 μm, and the quality of all crystals is verified using a 120mm path length. Note: Thallium salts are considered toxic and should be handled with care.

Product features：High numerical aperture, optimal collection efficiency 、 Compact single-lens design 、 Diffraction-limited design 、 RoHS certified

Application area：High numerical aperture, optimal collection efficiency 、 Compact single-lens design 、 Diffraction-limited design 、 RoHS certified

Unit Price

Please contact customer service for a discounted quote.

Part Number

MP-KRS5-50-4-W

Lead Time

Please contact customer service for lead time.

Stock

Please contact customer service for stock availability.

Add to Inquiry

Inquire online

General Parameters

Download Document

Dimensional Drawing

Parameter

Transmission wavelength range:	0 . 6 to 40 μm
Refractive index:	2 . 371 at 10 μm (1 )(3 )
Reflection loss:	28 . 4 %at 10 μm (2 surfaces)
Absorption coefficient:	n/ a
Rest strahlen Peak :	n/ a
dn/ dT :	-235 x 10^-6 / °C
dn/ d μ= 0 :	7 μm
Density:	7 . 371 g/ cc (3 )
Melting point:	414 . 5 °C (3 )
Thermal conductivity:	0 . 544 Wm^-1 K^-1 at 293K
Thermal expansion:	58 x 10^-6 / °C (2 )
Hardness:	Knoop 40 . 2 (2 )
Specific heat capacity:	200 J Kg^-1 K^-1at 273K
Dielectric constant:	32 . 5
Youngs Modulus (E) :	15 . 85 GPa (2 )
Shear modulus (G):	5 . 79 GPa (2 )
Bulk modulus (K):	19 . 78 GPa (2 )
Elastic modulus:	C_{1 1} =33 1 ; C₁₂ =13 . 2; C₄₄ =5 . 79
Apparent elastic limit:	26 . 2 MPa (2 )
Poisson's ratio:	0 . 369
Solubility:	0 . 05g/ 100g water at 293K
Molecular weight:	42 mole%Tl Br ; 58 mole%TlI
Category/structure:	Cubic , CsCl structure , Pm3m, No cleavage (3 )

Note 1: Warning: Thallium salts are toxic, so be careful when handling them.

No = Ordinary Ray

μm	No	μm	No	μm	No
0 . 54	2 . 68059	1 . 00	2 . 44620	1 . 50	2 . 40774
2 . 00	2 . 39498	3 . 00	2 . 38574	4 . 00	2 . 38204
5 . 00	2 . 37979	6 . 00	2 . 37797	7 . 0	2 . 37627
8 . 0	2 . 37452	9 . 0	2 . 37267	10 . 0	2 . 37069
1 1 . 0	2 . 36854	12 . 0	2 . 36622	13 . 0	2 . 36371
14 . 0	2 . 36101	15 . 0	2 . 35812	16 . 0	2 . 35502
17 . 0	2 . 35173	18 . 0	2 . 34822	19 . 0	2 . 34451
20 . 0	2 . 34058	21 . 0	2 . 33643	22 . 0	2 . 33206
23 . 0	2 . 32746	24 . 0	2 . 32264	25 . 0	2 . 31758
26 . 0	2 . 31229	27 . 0	2 . 30676	28 . 0	2 . 30098
29 . 0	2 . 29495	30 . 0	2 . 28867	31 . 0	2 . 28212
32 . 0	2 . 2753 1	33 . 0	2 . 26823	34 . 0	2 . 26087
35 . 0	2 . 25322	36 . 0	2 . 24528	37 . 0	2 . 23705
38 . 0	2 . 22850	39 . 0	2 . 21965	40 . 0	2 . 21047

Transmission curve

Original factory PN# example

Order PN#	Specific (D x L)(mm)	Diameter (D)	Thickness (L)	S/D	Material
KRS5P10-2	10.0mm×2.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P12X2	12.0mm×2.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P13-2	13.0mm×2.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P20-2	20.0mm×2.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P25-2	25.0mm×2.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P25-4	25.0mm×4.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P32-3D	32.0mm×3.0mm Punching	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P32-3	32.0mm×3.0mm Unpunched	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P35X2	35.0mm×2.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P42X3	42.0mm×3.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR
KRS5P50X4	50.0mm×4.0mm	+0.2/-0.0mm	±0.1mm	60/40	IR